APPLICATIONS
Epoxy curing agent for cathodic electrophoretic paint
Product name | Type | Color(Gardner) | Amine value(mgKOH/g) | Viscosity(cps,25℃) | Acid value(mgKOH/g) | Solid lacquer (%) | AHEW | Addition (phr)/100g resin | Gel time (min@25℃,150g mixture) | Film drying time (hrs@25℃) | Description |
BS8155 | Moditied polyamide | <12 | 250±10 | 15000-30000 | <3 | 98±2 | 145 | ----- | ----- | ----- | Medium viscosity, imine-based modified polyamide, long pot life, for solidification under high humidity condition, medium-thickness coating ana excellent salt fog resistance. Applicable for single-component and biocomponent cathode electropnresis paint. |
BS7156 | Modified polyamide | <12 | 250±20 | 8000-15000 | <3 | 98±2 | 145 | ----- | ----- | ----- | Imine-based modified polyamide, long Pot life, for solidification under high humidity condition.exceilent salt fog resistance. Applicable for single-component and biocomponent cathode electrophoresis paint. With viscosity lower than BS8155. |
BS6160 | Modified polyamide | <12 | 65±5 | 11500-17500Cps/20℃ | <3 | 70±1 | 550 | ----- | ----- | ----- | Medium viscosity, low amine value high molecular weight imine-based polyamide, long pot life, for solidification under high humidity condition, and excellent medium-thickness coating; applicable for single-component and biocomponent cathode electrophoresis paint. |
BS815LKK | Modified polyamide | <12 | 200±10 | 300-600 | <3 | 82±2 | 190 | ----- | ----- | ----- | Low viscosity imine-based polyamide, with long pot life and good adhesion, flexibility, chemical resistance, and low toxicity for the cured matter. |
BS815 | Polyamide | <12 | 310±20 | 8000-11000cps/40℃ | <3 | 98±2 | 125 | 66 | 124 | 10 | Medium viscosity, imine-free polyamide, long pot life, good flexibility and chemical resistance. |
BS815A | Polyamide | <12 | 310±20 | 8000-11000cps/40℃ | <3 | 98±2 | 125 | 66 | 110 | 8 | Imine-free polyamide, medium viscosity, and good adhesion, flexibility and rigidity for the cured matter. |
BS691 | Polyamide | <12 | 400 ±20 | 4000-7000cps/40℃ | <3 | 98±2 | 94 | 48 | 100 | 2.5 | Medium viscosity polyamide, for single-component cathode electrophoresis paint, and superior performance for the cured matter. |
BS8018 | Polyamide | <12 | 400 ±20 | 2500-4500 | <3 | 98±2 | 100 | 50 | 110 | 8 | Low viscosity polyamide, high amine value, good adhesion, flexibility and rigidity and long pot life. Applicable for single-component cathode electrophoresis paint. |
BS735 | Polyamide | <12 | 185±10 | 40000-70000cps/40℃ | <3 | 99±1 | 226 | 115 | 100 | 2.5 | High viscosity polyamide, for single-component and biocomponent cathode electrophoresis paint, and good salt fog. |
BS8037 | Polyamide | <12 | 200±10 | 3500-5500cps/75℃ | <3 | 99±1 | 190 | 100 | ----- | ----- | High viscosity polyamide, good adhesion, flexibility and rigidity. Generally applicable for bio-component cathode electrophoresis paint. |
BS8156 | Polyamide | <12 | 250±10 | 17000-23000 | <3 | 99±1 | 145 | ----- | ----- | ----- | Imine-free polyamide, medium viscosity, and good flexibility and excellent adhesion for the cured matter. Applicable for single-component cathode electrophoresis paint. |
BS1025 | Modified polyamide | <5 | 290±20 | <15 | ----- | ----- | 100 | ----- | ----- | ----- | Low viscosity, can be used longer time than BS1023M, curing under high humidity condition.Used for cathodic electrophoretic coatings and heavy-duty coating. |
BS1012M | Modified polyamide | <5 | 420±20 | 6-11 | ----- | ----- | 55 | ----- | ----- | ----- | Ketimine, for the specific marine, automotive maintenance, floor and adhesive. |
BS1013D | Modified polyamide | <5 | 480±20 | 1-15 | ----- | ----- | 55 | ----- | ----- | ----- | Ketimine with low viscosity, no oil free surface phenomena and fast curing rate (quicker than BS1012M). |
BS1023M | Modified polyamide | <5 | 450±20 | 5-15 | ----- | 98±2 | --- | ----- | 115 | ----- | Ketimine, with low viscosity and long pot life. Solidification under high humidity condition. |
BS1023M-73 | Modified polyamide | <5 | 330±20 | <15 | ----- | 73±2 | --- | ----- | ----- | ----- | Low viscosity, can use a long time, under the condition of high humidity curing. |
AP-10 | Polyether amine | <12 | 160±10 | 200-600 | ----- | 94±2 | 156 | 80 | ----- | ----- | High solid content, low viscosity, can use a long time, curing content has good flexibility, high elasticity and resistance to salt content. Used for electrophoresis paint coating |
AP-40 | Polyether amine | <12 | 40±20 | 200-600 | ----- | 98±2 | 577 | 294 | ----- | ----- | High molecular weight, high solid content, low viscosity, can use a long time, for electrophoretic coatings |